Yang, F; Chen, B; Hashimoto, T; Zhang, Y; Thompson, G; Robinson, I; (2019) Investigation of Three-Dimensional Structure and Pigment Surrounding Environment of a TiO2 Containing Waterborne Paint. Materials , 12 (3) , Article 464. 10.3390/ma12030464.

Preview

Text Fei_TiO2_Waterbourne_Materials.pdf - Accepted Version Download (3MB) | Preview

Abstract

Serial block-face scanning electron microscopy (SBFSEM) has been used to investigate the three-dimensional (3D) structure of a cured waterborne paint containing TiO2 pigment particles, and the surrounding environment of the TiO2 pigment particles in the cured paint film was also discussed. The 3D spatial distribution of the particles in the paint film and their degree of dispersion were clearly revealed. More than 55% of the measured TiO2 particles have volumes between 1.0 × 106 nm3 and 1.0 × 107 nm3. From the obtained 3D images, we proposed that there are three different types of voids in the measured cured waterborne paint film: voids that exist in the cured paint themselves, voids produced by particle shedding, and voids produced by quasi-liquid phase evaporation during measurement. Among these, the latter two types of voids are artefacts caused during SBFSEM measurement which provide evidence to support that the pigment particles in the cured paint/coating films are surrounding by quasi-liquid environment rather than dry solid environment. The error caused by particle shedding to the statistical calculation of the TiO2 particles was corrected in our analysis. The resulting 3D structure of the paint, especially the different voids are important for further systematic research, and are critical for understanding the real environment of the pigment particles in the cured paint films.

Download activity - last month

Export as JSONXMLCSV

Download activity - last 12 months

Export as XMLCSVJSON

Downloads by country - last 12 months

Export as JSONCSVXML

Archive Staff Only

View Item